摘 要：介紹了利用V 法鑄造工藝，使用中頻感應爐加精煉爐熔煉，采用底注開放式雙澆道的澆注系統，來生產高壓電器大型鋁筒體，分析了不同工藝參數對鑄造鋁筒體的影響。通過批量生產試驗驗證，為今后使用V 法鑄造生產鋁筒體提供了技術支持。
關鍵詞：高壓電器；鋁筒體；V 法鑄造；氣密性；工藝參數
中圖分類號：TM51 文獻標識碼：B 文章編號：1007-3175(2014)01-0051-03
Application of V Method Casting in High Voltage Electric Apparatus Aluminum Cylinder Production
WANG Shang, GU Xi-xiu
（Henan Pinggao Electric Co., Ltd, Pingdingshan 467 001, China）
Abstract: Introduction was made to that the high voltage electrical apparatus large-sized aluminum cylinder was produced by using V method casting technology , melting in medium frequency induction oven plus fining oven and adopting bottom pouring open type double pouring path pouring system. Analysis was made to the impacts of different technological parameters on casting aluminum cylinder. Batch production test verification has passed, which provides technical support for using V method to cast aluminum cylinder in the future.
Key words: high voltage electrical apparatus; aluminum cylinder; V method casting; air tightness; technological parameter